Product Description
State of the art, digital portable hardness tester is designed to test the hardness of cast,and large hard metal parts with rough surfaces. Loaded with useful functions only found on high priced models the PHT-1850 portable hardness tester is clearly setting a new industry standard by being the most accurate, economically priced portable hardness tester on the market today. Fast test speeds coupled with memory and output, this unit is a hands down winner whether you are out in the field or in the QC shop.
The PHT-1850 portable hardness tester can perform tests that easily convert to the most popular hardness scales, including Rockwell, Brinell, Vickers, Shore, etc.
Designed to test hardness on large cast parts and those with a rough surface:
Example: Mass of part should be equivalent to approximately 1 thick of solid steel where testing.
Operation:
Load the impact body
Place the impact body on your test piece
Push the button to begin testing and obtain reading
Standard Accessories:
Base instrument
Impact device G
Calibrated test block
Custom carry case
Cleaning brush
Operation manual
Optional accessories:
Impact devices; DC, D+15, DL, G, C
Special support rings
Mini Printer
Functions:
Easy to use keypad operation
Auto identification of Impact Device
Large LCD display with back light
USB Ouput
Automatic conversions to: Brinell, Rockwell B & C, Vickers and Shore
Automatic mean value as well as Min & Max values
Battery Indicator
Memory capacity (100 groups)
Specifications:
Accuracy: +/- 0.5% (referred to L=800,
Repeatability accuracy: +/- 4L units) L=Leeb
Measuring range: 200-960 HL
Materials: steel & cast steel, alloy tool steel, stainless steel, grey cast iron,
spheroidal iron, cast aluminum, brass, bronze, wrought copper alloy.
Battery type: AA alkaline (4)
Operating temperature: 5-104 degrees F
Dimensions: 150 x 74 x 32mm
Weight: 245 grams
Options:
NIST/ASTM certified hardness test blocks, penetrators and kits are available.
Impact device ->
G
Impact energy
90Nmm
Mass of the impact body
20g
Test tip
* Hardness
1600HV
* Diameter
5mm
* Material
Tungsten Carbide
Impact device
* Diameter
30mm
* Length
254mm
* Weight
250g
Max. hardness of sample
650HB
Preparation of surface
* Max. roughness depth Rt
30 m m
* Average roughness Ra
6.3 m m
Min. weight of sample
* Of compact shape
15kg
* On solid support
5kg
* Coupled on plate
0. 5kg
Indentation of test tip
With 300 HV
* Diameter
1.03mm
* Depth
53 m m
with 600 HV
* Diameter
0. 90mm
* Depth
41 m m